	High temperature corrosion performance of Q235 steel in sulfur-bearing solution
	Qin, Dahui; Qin, Yang; Mao, Ting; Liu, Jianjun; Liu, Fuzhen; Ma, Deying
发表日期	2016
ISSN	0960-3409
起始页码	94
结束页码	97
卷号	33 期号:1
英文摘要	The high temperature corrosion performance of Q235 steel in sulfur-bearing solutions as a function of temperature, test time, and sulfur content was investigated by weight loss measurements in this study. The results indicate that the corrosion behavior of Q235 steel in sulfur-bearing solution is directly related to the experimental temperature, immersion time and sulfur content. Higher temperature leads to a higher corrosion rate of the steel. The corrosion rate increases during the initial test time and then decreases with increasing the test time. As the sulfur content increases in the solution, the corrosion rate increases, and further increasing the sulfur content leads to a decreased corrosion rate.
英文关键词	High temperature corrosion; Sulfur corrosion; Carbon steel
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
来源期刊	MATERIALS AT HIGH TEMPERATURES
文献类型	期刊论文
条目标识符	http://gcip.llas.ac.cn/handle/2XKMVOVA/158558
作者单位	Qin, DH (corresponding author), Southwest Petr Univ, Sch Civil Engn & Architecture, Chengdu 610500, Peoples R China.; Qin, DH (corresponding author), Natl Engn Lab Oil & Gas Drilling Technol, Drill Bits Dept, Chengdu 610500, Peoples R China.
推荐引用方式 GB/T 7714	Qin, Dahui,Qin, Yang,Mao, Ting,et al. High temperature corrosion performance of Q235 steel in sulfur-bearing solution[J],2016,33(1).
APA	Qin, Dahui,Qin, Yang,Mao, Ting,Liu, Jianjun,Liu, Fuzhen,&Ma, Deying.(2016).High temperature corrosion performance of Q235 steel in sulfur-bearing solution.MATERIALS AT HIGH TEMPERATURES,33(1).
MLA	Qin, Dahui,et al."High temperature corrosion performance of Q235 steel in sulfur-bearing solution".MATERIALS AT HIGH TEMPERATURES 33.1(2016).